ExplosiveconsolidationofW-Cualloyaslinermaterials anditsperformance

摘要: 利用高能球磨制取W-Cu合金化粉末,采用爆炸烧结的方法制取W-Cu合金药型罩材料。爆炸烧结样品相对致密度达到99.6%,EPMA分析表明样品内各成分及元素分布均匀。对烧结样品作XRD分析, 计算其晶粒尺寸为26nm。使用固结样品加工成W-Cu合金药型罩,显示了良好的成形性。进行无隔板的静破甲实验,并与相同工艺条件下制取的纯Cu药型罩相比,其静破甲深度提高了31.8%。
- 爆炸力学|破甲能力|爆炸烧结|W-Cu合金 /
- 药型罩
Abstract: TheW-Cualloypowderswerepreparedbyhigh-energyball-milling.TheW-Cualloyaslinermaterialswasfabricatedbyexplosiveconsolidation. Theconsolidatedsamplehadatheoreticaldensityof99.6%. ThesamplewasdeterminedbyEPMA,andtheresultsshowedthatthecomposition anddistributionoftheelementswereuniform.ThesamplewasanalyzedbyXRDandtheWcrystallinesizesweremeasuredas26nm. ThesamplewasmachinedintoW-Cualloyliners,showinggood formingproperties.Quietarmor-piercingexperimentoftheW-Cualloylinerofshapedchargewithout aninsulatingboardindicatesthatthearmor-piercingcapabilityincreasesby31.8percentincomparisonwiththecopperliner.
- mechanicsofexplosion /
- armor-piercingcapability

1.	张金波，杨明川，王猛，刘子禛. 雾化干燥法制备钨铜药型罩材料. 中国新技术新产品. 2023(10): 4-7 . 百度学术
2.	陈翔，李晓杰，缪玉松，闫鸿浩，王小红. 爆炸压实/扩散烧结法制备钨铜梯度材料. 爆炸与冲击. 2019(01): 131-139 . 本站查看
3.	刘海龙，曲家惠，杨明川，卢凤生，彭琳茜，李岩. 湿化学法制备Cu-20%W药型罩材料的研究. 沈阳理工大学学报. 2017(01): 25-27+37 . 百度学术
4.	刘麒峰，赵捍东，王金虎. W-Cu复合药型罩EFP的形成及其聚能破甲效应研究. 兵器材料科学与工程. 2015(06): 102-105 . 百度学术
5.	刘迎彬，沈兆武，刘天生，胡晓艳，孙素杰. 钨铜药型罩制备及其侵彻性能研究. 实验力学. 2012(05): 618-622 . 百度学术