谭子翰, 徐松林, 章超, 胡时胜. 不同温度下2种钨结构增强Zr基非晶合金的动态压缩性能[J]. 爆炸与冲击, 2013, 33(3): 225-230. doi: 10.11883/1001-1455(2013)03-0225-06
引用本文: 谭子翰, 徐松林, 章超, 胡时胜. 不同温度下2种钨结构增强Zr基非晶合金的动态压缩性能[J]. 爆炸与冲击, 2013, 33(3): 225-230. doi: 10.11883/1001-1455(2013)03-0225-06
Tan Zi-han, Xu Song-lin, Zhang Chao, Hu Shi-sheng. Dynamic compressive properties of two tungsten structure reinforced Zr-based metallic glass composites at different temperatures[J]. Explosion And Shock Waves, 2013, 33(3): 225-230. doi: 10.11883/1001-1455(2013)03-0225-06
Citation: Tan Zi-han, Xu Song-lin, Zhang Chao, Hu Shi-sheng. Dynamic compressive properties of two tungsten structure reinforced Zr-based metallic glass composites at different temperatures[J]. Explosion And Shock Waves, 2013, 33(3): 225-230. doi: 10.11883/1001-1455(2013)03-0225-06

不同温度下2种钨结构增强Zr基非晶合金的动态压缩性能

doi: 10.11883/1001-1455(2013)03-0225-06
详细信息
    通讯作者:

    徐松林

Dynamic compressive properties of two tungsten structure reinforced Zr-based metallic glass composites at different temperatures

  • 摘要: 利用SHPB装置对钨丝增强Zr基非晶复合材料和钨骨架增强Zr基非晶复合材料进行了3种环境温度下多种应变率的动态压缩性能测试。比较了2种材料的动态力学性能,发现二者均具有应变率敏感性和较强的塑性变形能力。但二者承载机制存在较大差异。钨丝增强结构变形主要表现在钨丝的失稳,由数值模拟初步分析了这种局部结构失稳控制的变形以及热失稳现象;钨骨架增强结构变形前期钨骨架起主要承载作用,而不是各成分的共同作用,这导致材料的屈服强度比纯非晶和纯钨的低。