Dynamic behavior and constitutive model of phenolic cotton fabric material under impact loading
-
摘要: 为了研究酚醛层压材料的冲击力学行为并获得本构模型，利用万能试验机和整形修正的分离式霍普金森压杆(SHPB)装置，对材料试样进行了应变率范围为10-3~103 s-1的单轴压缩实验，得到了不同加载应变率下的应力应变曲线，对其在准静态、动态载荷下的压缩破坏机理进行了初步探讨。结果表明，酚醛层压材料具有较强的应变率效应，与准静态(1.67×10-3 s-1)时相比，在动态载荷(7×102 s-1)下，峰值应力增加了约10倍；破坏应变减少了约一半；在准静态和动态加载条件下试样力学性能的差异是由于纤维基体界面特性以及不同应变率下破坏模式的不同；采用朱-王-唐本构方程描述了酚醛层压材料力学行为，拟合得到了本构方程的系数，在加载过程中，理论计算值与实验结果吻合较好。Abstract: In order to obtain mechanical properties of phenolic cotton fabric material at different strain rates, we performed experiments of the uniaxial compression tests of phenolic cotton fabric material at the strain rate ranging from 10-3 to 103 s-1, using the universal testing machine and the split Hopkinson pressure bar (SHPB), obtained the stress-strain curve at different strain rates, and discussed compression failure mechanism under quasi-static and dynamic loads. The results from our experiments show that the dynamic compression fail strength of phenolic cotton fabric material has strong strain rate sensitivity and it increases along with the strain rate. Compared with the stress under the quasi-static loading, the peak stress under the dynamic loading increases by approximately 10 times, while the failure strain is reduced to about half. The differences in the mechanical properties under quasi-static and dynamic loading conditions is due to the strain rate effect of the fiber matrix interface characteristics on the one hand, and to the differences in failure modes at different strain rates on the other. Zhu-Wang-Tang (ZWT) constitutive was adopted to describe the mechanical behavior of the phenolic cotton fabric material.
-
图 3 动态压缩下不同应变率的应力应变曲线
Figure 3. Stress-strain curves of impact experiment at high speed
图 4 准静态压缩下不同应变率下的应力应变曲线
Figure 4. Stress-strain curves of impact experiment at low speed
-
[1] 孙朝翔, 鞠玉涛, 胡少青, 等.聚碳酸酯高应变率分离式霍普金森压杆实验研究[J].南京理工大学学报, 2012, 36(3): 529-533. http://www.cnki.com.cn/Article/CJFDTotal-NJLG201203029.htmSun Chao-xiang, Ju Yu-tao, Hu Shao-qing, et al. Experimental investigation of polycarbonate at high strain rate by SHPB[J]. Journal of Nanjing University of Science and Technology, 2012, 36(3): 529-533. http://www.cnki.com.cn/Article/CJFDTotal-NJLG201203029.htm [2] 谢中秋, 张蓬蓬. PMMA材料的动态压缩力学特性及应变率相关本构模型研究[J].实验力学, 2013, 28(2): 220-226. http://www.cqvip.com/QK/91138X/20132/45886843.htmlXie Zhong-qiu, Zhang Peng-peng. On the dynamic compressive mechanical properties and strain rate related constitutive model of PMMA material[J]. Journal of Experimental Mechanics, 2013, 28(2): 220-226. http://www.cqvip.com/QK/91138X/20132/45886843.html [3] 管公顺, 王少恒, 成方圆.不同加载应变率下有机玻璃的压缩破坏与力学行为[J].航空材料学报, 2012, 32(6): 96-101. http://d.wanfangdata.com.cn/Periodical/hkclxb201206016Guan Gong-shun, Wang Shao-heng, Cheng Fang-yuan. Compression failure and mechanics behavior of PMMA under different loading strain rates[J]. Journal of Aeronautical Materials, 2012, 32(6): 96-101. http://d.wanfangdata.com.cn/Periodical/hkclxb201206016 [4] 王礼立, 施绍裘, 陈江瑛, 等. ZWT非线性热粘弹性本构关系的研究与应用[J].宁波大学学报:理工版, 2000, 13: 141-149. http://www.cqvip.com/Main/Detail.aspx?id=4997411Wang Li-li, Shi Shao-qiu, Chen Jiang-ying, et al. ZWT non-linear thermo-viscoelastic constitutive relationship between research and application[J]. Journal of Ningbo University: Natural Science & Engineering Edition, 2000, 13: 141-149. http://www.cqvip.com/Main/Detail.aspx?id=4997411 [5] 王礼立, Pluvinage G, Labibes K.冲击载荷下高聚物动态本构关系对粘弹性波传播特性的影响[J].宁波大学学报, 1995, 8(3): 30-57. http://www.cnki.com.cn/Article/CJFDTotal-NBDZ503.005.htmWang Li-li, Pluvinage G, Labibes K. The influence of dynamic constitutive relations of polymers at impact loading on the viscoelastic wave propagation character[J]. Journal of Ningbo University, 1995, 8(3): 30-57. http://www.cnki.com.cn/Article/CJFDTotal-NBDZ503.005.htm [6] 邹广平, 杨继, 王瑞瑞, 等.聚氨酯夹芯整体层连复合材料的力学性能研究[J].哈尔滨工业大学学报, 2011, 43: 257-261. http://www.cqvip.com/QK/90629X/2011S1/1003576966.htmlZou Guang-ping, Yang Ji, Wang Rui-rui, et al. Experimental investigation on mechanical properties of the integrated hollow core sandwich composite filling polyurethane[J]. Journal of Harbin Institute of Technology, 2011, 43: 257-261. http://www.cqvip.com/QK/90629X/2011S1/1003576966.html [7] Forquin P, Nasraoui M, Rusinek A. Experimental study of the confined behavior of PMMA under quasi-static and dynamic loading[J]. International Journal of Impact Engineering, 2012, 40/41(1): 46-57. http://www.sciencedirect.com/science/article/pii/S0734743X11001473 [8] 宋力, 胡时胜. SHPB数据处理中的二波法与三波法[J].爆炸与冲击, 2005, 25(4): 368-373. doi: 10.11883/1001-1455(2005)04-0368-06Song Li, Hu Shi-sheng. Two-wave and three-wave method in SHPB data processing[J]. Explosion and Shock Waves, 2005, 25(4): 368-373. doi: 10.11883/1001-1455(2005)04-0368-06 [9] Zhang H D, Zhu Z W, Song S C, et al. Dynamic behavior of frozen soil under uniaxial strain and stress conditions[J]. Applied Mathematics and Mechanics: English Edition, 2013, 34(2): 229-238. doi: 10.1007/s10483-013-1665-x [10] Christmann A, Ienny P, Quantin J C, et al. Mechanical behavior at large strain of polycarbonate nanocomposites during uniaxial tensile test[J]. Polymer, 2011, 52(18): 4033-4044. doi: 10.1016/j.polymer.2011.06.056 [11] 王鹏飞, 胡时胜.轴向尺寸对泡沫铝动静态力学性能的影响[J].爆炸与冲击, 2012, 32(4): 393-398. doi: 10.11883/1001-1455(2012)04-0393-06Wang Peng-fei, Hu Shi-sheng. Mechanical properties of foam aluminum with different sizes[J]. Explosion and Shock Waves, 2012, 32(4): 393-398. doi: 10.11883/1001-1455(2012)04-0393-06 [12] Capan I, Tarimci C, Hasasan A K. Characterization and optical vapour sensing properties of PMMA thin films[J]. Materials Science and Engineering: C, 2009, 29(1): 140-143. http://www.sciencedirect.com/science/article/pii/S0928493108001185 [13] 胡泽斌, 许金余, 席峰, 等. EPS混凝土的冲击力学行为及本构模型[J].振动与冲击, 2011, 30(2): 65-68. http://d.wanfangdata.com.cn/Periodical/zdycj201102013Hu Ze-bin, Xu Jin-yu, Xi Feng, et al. Dynamic behavior and constitutive model of styropor concrete under impact loading[J]. Journal of Vibration and Shock, 2011, 30(2): 65-68. http://d.wanfangdata.com.cn/Periodical/zdycj201102013 [14] Casem D, Weerasooriya T, Moy P. Inertia effects of quartz force transducers embedded in a split Hopkinson pressure bar[J]. Experimental Mechanics, 2005, 45: 368-376. doi: 10.1007/BF02428167 期刊类型引用(1)
1. 张亚锋，张韶华，周刚，张激扬，卿涛，周宁宁. 多孔棉布-酚醛轴承保持架的应变速率敏感性. 西南交通大学学报. 2021(04): 847-852+863 . 
百度学术其他类型引用(1)
-
下载:
百度学术推荐阅读
不同冷却方式下高温混凝土的动态力学特性
吴栩霆 等, 爆炸与冲击, 2025
高速冲击下混凝土动力学性质和动态温度研究
黄晨瑞 等, 爆炸与冲击, 2025
不同应变率下皮质骨压缩力学实验与本构模型
徐诚意 等, 爆炸与冲击, 2025
泡沫混凝土弹塑性损伤模型在组合式防护结构中的应用
时述峰 等, 爆炸与冲击, 2024
聚酰亚胺的动静态压缩力学性能及本构模型
于文峰 等, 高压物理学报, 2022
玻璃纤维增强聚碳酸酯复合材料的动态拉伸力学行为特征及其失效机理
管海陆 等, 高压物理学报, 2023
冲击载荷下分支交错层状仿生复合材料动态断裂行为的实验研究和数值模拟
张海广 等, 高压物理学报, 2022
The role of silicon in drug discovery: a review
Panayides, Jenny-Lee et al., RSC MEDICINAL CHEMISTRY, 2024
Mechanical response behavior, constitutive modeling and microstructural evolution of a 7003-t6 al alloy rolled plate under high-speed impact loading
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2025
Global yield surface construction of polymethacrylimide foam by an integrated approach combining nanoindentation, machine learning and microstructure-informed modeling
MATERIALS & DESIGN, 2025
Powered by 
图(7)
计量
- 文章访问数: 3303
- HTML全文浏览量: 460
- PDF下载量: 626
- 被引次数: 2